Zirlux Anterior Multi

Multi-Layered Zirconia with more indications and strength than Lithium Disilicate

Zirlux Anterior Multi is a multilayered Zirconia with fully gradient shading that matches the incisal, dentin, and gingiva of dentition—making it suitable for anterior restorations. The transition of layers mimics the translucency and esthetics of a natural tooth without adding the necessary steps to the workflow. Zirlux Anterior Multi can be characterized after sintering for cases that require additional customization.

Buy Now

Indications

  • Full Contour Crowns
  • 2-3 Unit Bridges
  • Telescopic Crowns
  • Veneers

Highlights

  • Axially pressed zirconia followed by cold isostatic pressing using even pressure from every direction creates consistency and ensures the finest quality.
  • Each disc is quality checked before final packaging to ensure the material is of the highest quality.
  • Compatible with Roland, Amann Girrbach, and most open 98.5mm CAD/CAM Milling Machines.

Physical Characteristics

  • Density before sintering: ≥6.0 g/cm3
  • CTE after sintering (25-500°C): (10.5 ± 1.0) x10 -6K-1
  • 3-point flexural strength after sintering: 600 MPa
  • Accelerated aging surface monoclinic phase content: <5%
  • Chemical solubility after sintering: <100ug/cm2
  • Cytotoxicity test: 0 level
  • Radioactivity after sintering: <0.1Bq/g
  • Sintering temperature: 1430~1470°C1450°C recommended

Chemical Composition

  • ZrO2 + HfO2: 86.3%-94.2%
  • Y2O3: 5.8%-9.7%
  • Er2O3: <2%
  • Fe2O3: <0.5%
  • AI2O3: <0.5%
  • Other Oxides: <0.5%0